A4001 50A(道康寧熱塑性彈性體TPE TPR)

關(guān)鍵詞：A4001 50A，TPSIV，熱塑彈性體
MULTIFLEX® A 4001 50 A NAT 59150

Compatibility / 結(jié)合材料: ABS/ASA/SAN/PMMA/PC/PETg/PS/HIPS 

Process / 加工: Injection/Extrusion, 注塑/擠塑

Other information/其它信息: EN71-3 met/符合EN71-3標(biāo)準(zhǔn)；FDA met/符合FDA標(biāo)準(zhǔn)   

PROPERTIES / 性能UNITS / 單位STANDARDS / 標(biāo)準(zhǔn)Average Values / 平均值
Hardness 硬度Shore A 邵氏 AISO 868 - MDA 110  50
Density 密度g/cm3 克/厘米3ISO R1183 - MDA 1121.03
Spiral flow 螺旋注塑長(zhǎng)度Cm /厘米MD17956
Tensile strength at 100% elongation
100%伸長(zhǎng)率時(shí)的抗拉強(qiáng)度
Flow Direction 縱向
Transverse Direction 橫向		MPa 兆帕ISO 37 - MDA 121--
Tensile strength at 200% elongation
200%伸長(zhǎng)率時(shí)的抗拉強(qiáng)度
Flow Direction 縱向
Transverse Direction 橫向		MPa 兆帕ISO 37 - MDA 121--
Tensile strength at 300% elongation
300%伸長(zhǎng)率時(shí)的抗拉強(qiáng)度
Flow Direction 縱向

Transverse Direction 

橫向

MPa 兆帕ISO 37 - MDA 121--
Tensile strength at break
斷裂時(shí)的抗拉強(qiáng)度
Flow Direction 縱向
Transverse Direction 橫向		MPa 兆帕ISO 37 - MDA 1213.5
2.5

Elongation at break
斷裂時(shí)的伸長(zhǎng)率
Flow Direction 縱向
Transverse Direction 橫向

%ISO 37 - MDA 121

>500                                     

>500


Tear Strength 抗撕裂強(qiáng)度
Flow Direction 縱向
Transverse Direction 橫向

KN/m²
千牛頓/米2		ISO 34  - MDA 12123.0
15.0

The MDA (Méthode D’Analyse) named in this document are issued from the ISO Standards. 表中所提及的 MDA (Méthode D’Analyse) 是由 ISO 頒布的標(biāo)準(zhǔn)。  
The values mentioned in this Technical Data Sheet are issued from test bars realized on specific equipment, in conformity with normalized standards. Although we estimate that these information are exact, it is important to know that under other conditions with another equipment than our, the results can be appreciably different.

Therefore we are not responsible when those information are not interpreted as they should be.

產(chǎn)品規(guī)格中所列的各項(xiàng)數(shù)據(jù)是由特別的儀器遵照標(biāo)準(zhǔn)化測(cè)試所得到的。 盡管我們認(rèn)為這些信息是準(zhǔn)確的， 但是如果在其它的情況下由其它的儀器所測(cè)得的數(shù)據(jù)可能有所不同， 所以， 客戶應(yīng)該自行確認(rèn)產(chǎn)品可否被采用。

Dow Corning Corporation  

產(chǎn)品加工指南(注塑) / PRODUCT MOLDING GUIDE
                  MULTIFLEX® A 4001 50 A NAT 59150


§Temperature Profile / 加工溫度:

REAR 后段CENTER 中段FRONT 前段NOZZLE 射嘴MOLD 模具
165°C175°C180°C185°C30°C


* All temperature at +/-10 °C, 所有加工溫度可以在正負(fù)10攝氏度之間調(diào)節(jié)

§Predrying advice / 干燥建議 : 

Temperature 溫度Time時(shí)間
60°C2 hours/小時(shí)



§Injection speed / 注塑速度 :    Middle to High / 中 至 快速

§Injection  and back pressure / 注塑壓力和背壓 :

Injection pressure 注塑壓力Back pressure 背壓
30-80 Bar3-20 Bar


§ Cooling time / 冷卻時(shí)間 :
5-15 second / 5-15 秒


§ Coloring Masterbatch/Pigment Powder selection / 色母粒/色粉選擇建議 :
We recommend using pigment powder or EVA based coloring masterbatch. Please avoid using PE or PP based coloring masterbatch.
我們建議在該材料的配色過(guò)程中使用色粉，或者使用以EVA為載體的色母粒。請(qǐng)?jiān)谂渖^(guò)程中盡量避免使用PE或PP為載體的色母粒，以免影響材料和工程塑料之間的粘合能力。